Porous wall ceramics with burnout additive from flax boon

Abstract

Advantages and technologies of porous ceramics production are considered. the experience of using burnout additives of different origin for wall ceramics is analyzed. in the work it is proposed to use a flax boon fraction of not more than 2 mm as a burnout additive. Density and strength of ceramic samples were determined. the dependence of the average density and strength of the ceramic shard on the consumption of flax boon, including the use of superplasticizer S-3. the positive effect of the use of superplasticizer S-3 on the compressive strength of porous ceramic samples was established. the data on frost resistance and thermal conductivity of porous wall ceramics samples obtained by using flax boon as a burnout additive are presented.= Рассмотрены преимущества и технологии производства стеновой пористой керамики. Проанализирован опыт применения выгорающих добавок растительного происхождения для стеновой керамики. Предлагается использовать костру льна фракцией не более 2 мм в качестве выгорающей добавки. Определены плотность и прочность керамических образцов. Установлена зависимость средней плотности и прочности керамического черепка от расхода костры льна, в том числе при использовании суперпластификатора С-3. Установлено положительное влияние применения суперпластификатора С-3 на прочность при сжатии пористых керамических образцов. Приведены данные по морозостойкости и теплопроводности образцов пористой стеновой керамики, полученных с использованием костры льна в качестве выгорающей добавки.